| Liquid viscosity | 150-300 MPa·s 25℃ / Rotational viscometer |
| Liquid density | 1.05-1.25 g/cm³ 25℃ / Densitometer |
| Flexural modulus | 1.882-2.385 MPa |
| Bending strength | 40-70MPa |
| Heat distortion temperature | 80℃ |
| Thermal expansion coefficient | 95*E-6 |
| Volume shrinkage | 3.72-4.24% |
| Linear shrinkage | 1.05-1.35% |
| Tensile strength | 30-52Mpa |
| Tensile modulus | 1.779-2.385MPa |
| Stretch ratio | 120% |
| Shore hardness | 65-75D |
| Glass transition temperature | 100℃ |
| Density after curing | 1.05-1.25g/cm3 |
| Notched impact strength | 41-48j/m |
| Optimal storage temperature | 20℃～25℃ |
| Curing wavelength | 405nm |
| Material color | Transparent |
| Product net weight | 500ml/bottle * 2 |
| Product gross weight | 1.5kg |
| Packing size | 215(L)×125(W)×220(H)mm |